Aluminum 6061-T651 | 3.3211 | 65028 | AlMg1SiCu
Property Value Mechanical Properties Ultimate tensile strength 290 – 330 MPa Yield strength 250 – 270 MPa Elongation at break 8 – 11 % Physical Properties Corrosion resistance High Magnetism Non-magnetic Weldability High Thermal Properties Maximum service temperature 170 °C Thermal conductivity 167 – 170 W/(m⋅°C) Post Treatments Post-Processing Annealing & Cold working Anodizing compatibility […]
Aluminum 7075-T7351 | 3.4365 | 76528 | AlZn5.5MgCu
Property Value Mechanical Properties Ultimate tensile strength 460 – 510 MPa Yield strength 385 – 410 MPa Elongation at break 6 – 8 % Physical Properties Corrosion resistance Moderate Magnetism Non-magnetic Weldability Poor Thermal Properties Thermal conductivity 130 – 155 W/(m⋅°C) Post Treatments Anodizing compatibility Not recommended – due to the high amount of zinc […]
Tool steel D2 | 1.2379 | X153CrMoV12-1 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 758 – 860 MPa Yield strength 420 – 470 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 16 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Maximum service temperature 195 – 245 °C Thermal expansion coefficient 10.3 – 12 × 10-6/ºC Thermal conductivity 29.3 […]
Tool steel A2 | 1.2363 | X100CrMoV5-1- Annealed state
Property Value Mechanical Properties Ultimate tensile strength 670 – 710 MPa Yield strength 345 – 350 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 % Physical Properties Magnetism Magnetic Weldability Moderate Thermal Properties Maximum service temperature 195 – 245 °C Thermal expansion coefficient 10.5 – 11 × 10-6/ºC Thermal conductivity 36.1 […]
Tool steel O1 | 1.2510 | 100MnCrW4 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 640 – 720 MPa Yield strength 400 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 20 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Maximum service temperature 165 – 215 °C Thermal expansion coefficient 11.3 – 11.8 × 10-6/ºC Thermal conductivity 41.2 – 44.6 […]
Tool steel A3 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 700 MPa Yield strength 340 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 % Physical Properties Corrosion resistance Poor Magnetism Magnetic Weldability Poor Thermal Properties Thermal expansion coefficient 11.8 – 14.3 × 10-6/ºC Thermal conductivity 37 W/(m⋅°C) Post Treatments Post-Processing Cold work, Annealing, Quenching, […]
Tool steel S7 | 1.2355 | 50CrMoV13-15 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 640 – 670 MPa Yield strength 370 – 380 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 – 25 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Maximum service temperature 165 – 215 °C Thermal expansion coefficient 10.7 – 11.2 × 10-6/ºC Thermal […]
Tool steel H13 | 1.2344 | X40CrMoV5-1 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 690 MPa Yield strength 330 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Thermal expansion coefficient 10.4 – 12.4 × 10-6/ºC Thermal conductivity 22 – 29 W/(m⋅°C) Electrical Properties Electrical resistivity 52 – 86 μΩ*cm […]
Titanium Grade 5 | 3.7164 | Ti6Al4V
Property Value Mechanical Properties Ultimate tensile strength 920 – 1000 MPa Yield strength 830 – 880 MPa Young’s modulus (modulus of elasticity) 113.8 GPa Elongation at break 9 – 11 % Hardness 334 HB Physical Properties Corrosion resistance Very high Magnetism Low Common Applications Aerospace
Titanium Grade 1 | 3.7025
Property Value Mechanical Properties Ultimate tensile strength 310 – 350 MPa Yield strength 220 – 240 MPa Young’s modulus (modulus of elasticity) 103 – 105 GPa Elongation at break 28 – 32 % Hardness 120 HB Physical Properties Corrosion resistance Excellent Magnetism Non-magnetic Weldability High Thermal Properties Maximum service temperature 320 – 400 °C Thermal […]