FR4
Property Value Mechanical Properties Ultimate tensile strength 240 – 310 MPa Young’s modulus (modulus of elasticity) 12 – 27 GPa Elongation at break 0.008 – 0.01 % Hardness 100 – 110 HRM Physical Properties UV resistance Good Thermal Properties Maximum service temperature 122 – 145 °C Thermal expansion coefficient 9.9 – 11.9 × 10-6/ºC Thermal […]
ABS
Property Value Mechanical Properties Ultimate tensile strength 27.6 – 55.2 MPa Yield strength 18.5 – 51 MPa Young’s modulus (modulus of elasticity) 1.1 – 2.9 GPa Elongation at break 10 – 50 % Hardness 5.6 – 15.3 HV Physical Properties UV resistance Poor Thermal Properties Maximum service temperature 61.9 – 76.9 °C Thermal expansion coefficient […]
Aluminum 5052 | EN AW-5052 | 3.3523 | AlMg2,5
Property Value Mechanical Properties Ultimate tensile strength 170 – 210 MPa Yield strength 70 – 120 MPa Young’s modulus (modulus of elasticity) 68 – 71 GPa Elongation at break 7 – 20 % Physical Properties Corrosion resistance Good Magnetism Non-magnetic Thermal Properties Maximum service temperature 190 °C Thermal expansion coefficient 23.8 – 25.7 × 10-6/ºC […]
Aluminum 2024-T351 | 3.1355 | 24530 | AlCu4Mg1
Property Value Mechanical Properties Ultimate tensile strength 395 – 470 MPa Yield strength 275 – 310 MPa Young’s modulus (modulus of elasticity) 71 – 73.1 GPa Elongation at break 9 – 15 % Physical Properties Corrosion resistance Poor Magnetism Non-magnetic Weldability Good Thermal Properties Maximum service temperature 200 °C Thermal expansion coefficient 23 – 24.7 […]
Aluminum 7050 | EN AW-7050 | 3.4144| AlZn6CuMgZr
Property Value Mechanical Properties Ultimate tensile strength 395 – 470 MPa Yield strength 275 – 310 MPa Young’s modulus (modulus of elasticity) 71 – 73.1 GPa Elongation at break 9 – 15 % Physical Properties Corrosion resistance Poor Magnetism Non-magnetic Weldability Good Thermal Properties Maximum service temperature 200 °C Thermal expansion coefficient 23 – 24.7 […]
Aluminum MIC6Aluminum
Property Value Mechanical Properties Ultimate tensile strength 160 – 170 MPa Yield strength 70 – 130 MPa Young’s modulus (modulus of elasticity) 71 GPa Elongation at break 3 – 7 % Physical Properties Corrosion resistance Good Magnetism Non-magnetic Weldability Good Thermal Properties Maximum service temperature 427 °C Thermal expansion coefficient 23.6 – 24.5 × 10-6/ºC […]
Aluminum 6082-T651 | 3.2315 | 64430 | AlSi1MgMn
Property Value Mechanical Properties Ultimate tensile strength 275 – 320 MPa Yield strength 240 – 270 MPa Elongation at break 6 – 10 % Thermal Properties Thermal conductivity 170 W/(m⋅°C) Post Treatments Anodizing compatibility Suitable Common Applications Structural components Trusses Heat sinks
Aluminum 2017A | 3.1325 | 24530 | AlCu4MgSi
Property Value Mechanical Properties Ultimate tensile strength 250 – 400 MPa Yield strength 110 – 270 MPa Young’s modulus (modulus of elasticity) 16 – 19 GPa Elongation at break 14 – 22 % Physical Properties Corrosion resistance Fair Magnetism Non-magnetic Weldability Good Thermal Properties Maximum service temperature 190 °C Thermal expansion coefficient 23.6 – 25.4 […]
Aluminum 7075-T651 | 3.4365 | 76528 | AlZn5.5MgCu
Property Value Mechanical Properties Ultimate tensile strength 520 – 560 MPa Yield strength 460 – 470 MPa Elongation at break 6 – 9 % Thermal Properties Thermal conductivity 130 W/(m⋅°C) Post Treatments Anodizing compatibility Not recommended – due to the high amount of zinc that the material contains, dark spots or corroded marks may be […]
Aluminum 2014 | 3.1255 | 24345 | AlCu4SiMg
Property Value Mechanical Properties Ultimate tensile strength 190 – 245 MPa Yield strength 100 – 125 MPa Young’s modulus (modulus of elasticity) 72 – 73.3 GPa Elongation at break 11 – 16 % Physical Properties Corrosion resistance Poor Magnetism Non-magnetic Weldability Fair Thermal Properties Maximum service temperature 210 °C Thermal expansion coefficient 23 – 24.4 […]