PP+GF(30%)PP+GF(30%)
Property Value Mechanical Properties Ultimate tensile strength 68 – 85 MPa Young’s modulus (modulus of elasticity) 6.5 – 7 GPa Elongation at break 2.1 – 3.4 % Hardness 110 HRC Physical Properties UV resistance Fair Thermal Properties Maximum service temperature 100 °C Thermal expansion coefficient 25 – 70 × 10-6/ºC Thermal conductivity 0.27 – 0.3 […]
PP Homopolymer
Property Value Mechanical Properties Yield strength 19 – 30 MPa Young’s modulus (modulus of elasticity) 0.7 – 1.2 GPa Elongation at break min. 50 % Thermal Properties Maximum service temperature 80 °C Common Applications Chemical technology Piping Packaging
PP
Property Value Mechanical Properties Ultimate tensile strength 23 – 33 MPa Yield strength 30 – 32 MPa Young’s modulus (modulus of elasticity) 0.9 – 1.6 GPa Elongation at break 8 – 12 % Hardness 65 – 102 HRR Physical Properties UV resistance Poor Thermal Properties Maximum service temperature 80 – 130 °C Thermal expansion coefficient […]
test
Acetal Copolymer (POM-C)
Property Value Mechanical Properties Ultimate tensile strength 60 – 70 MPa Yield strength 60 – 67 MPa Young’s modulus (modulus of elasticity) 2.5 – 2.7 GPa Elongation at break 30 – 32 % Hardness 88 HRM Physical Properties UV resistance Poor Thermal Properties Maximum service temperature 82 – 90 °C Thermal expansion coefficient 90 – […]
Acetal Copolymer (POM-C) FDA
Property Value Mechanical Properties Yield strength 66 – 70 MPa Young’s modulus (modulus of elasticity) 2.8 – 3 GPa Elongation at break 32 – 40 % Thermal Properties Maximum service temperature 100 – 140 °C Thermal conductivity 0.31 – 0.39 W/(m⋅°C) Common Applications Components with contact to water Food or pharmaceuticals
Acetal Homopolymer (POM-H)
Property Value Mechanical Properties Ultimate tensile strength 60 – 89.6 MPa Yield strength 48.6 – 72.4 MPa Young’s modulus (modulus of elasticity) 2.5 – 4 GPa Elongation at break 15 – 75 % Hardness 14.6 – 24.8 HV Physical Properties UV resistance Poor Thermal Properties Maximum service temperature 76.9 – 96.9 °C Thermal expansion coefficient […]
Acetal Copolymer (POM-C) ESD
Property Value Mechanical Properties Yield strength 45 MPa Elongation at break 40 – 50 % Thermal Properties Maximum service temperature 100 – 140 °C Thermal expansion coefficient 10 – 13 × 10-6/ºC Thermal conductivity 0.3 W/(m⋅°C) Electrical Properties Electrical resistivity 10 μΩ*cm Common Applications Tool carriers Housing parts Rollers
PTFE
Property Value Mechanical Properties Ultimate tensile strength 25 – 31 MPa Yield strength 14 – 41.4 MPa Young’s modulus (modulus of elasticity) 0.39 – 2.25 GPa Elongation at break 300 – 450 % Hardness 50 – 65 Shore D Physical Properties UV resistance Good Thermal Properties Maximum service temperature 250 – 270 °C Thermal expansion […]
HDPE
Property Value Mechanical Properties Ultimate tensile strength 22.1 – 31 MPa Yield strength 26.2 – 31 MPa Young’s modulus (modulus of elasticity) 1.07 – 1.09 GPa Elongation at break 500 – 700 % Hardness 7.9 – 9.9 HV Physical Properties UV resistance Moderate Thermal Properties Maximum service temperature 113 – 129 °C Thermal expansion coefficient […]